Objektif: Kantite diferans ki genyen ant carbure ak foure seramik lè fini -vire lam turbine Inconel 718 anba presyon likid refwadisman etaj pwodiksyon-(7 MPa).
Metòd: Yon sèl -pwen, plen-faktoral jijman varye vitès koupe (vc 40-120 m/min) ak manje (fn 0.05-0.20 mm/r). Pwen fen lavi zouti -te 0.3 mm usure flan oswa katastwofik ka zo kase. Yo te anrejistre pouvwa, brutality sifas (Ra) ak pwofondè kouch blan{10}}.
Rezilta: Nan vc 80 m/min, moustach-foisye seramik ranfòse te kouri 2.1 min anvan ka zo kase men retire 4.8× materyèl carbure kouvwi (GC1115) ki te dire 11 min. Carbide pwodui Ra 0.42 µm kont 0.78 µm pou seramik. Pwofondè kouch-blan te rete anba a 5 µm pou tou de.
Konklizyon: Seramik yo triple MRR lè vitès Pi gran pase oswa egal a 80 m/min ak sifas Ra Mwens pase oswa egal a 0.8 µm akseptab; carbure rete pi an sekirite pou Ra < 0.5 µm oswa koupe koupe.
Carbide Insert vs seramik Insert pou Superalloy Turbine Lam
Lam superalliaj ki baze sou nikèl- kite forge a nan 46 HRC epi manje bidjè zouti pou manje maten. Boutik yo anjeneral chwazi ant carbure ultra-difisil ak flanm-fois seramik rapid san nimewo difisil. Nòt sa a bay nimewo sa yo-pa gen okenn bagay maketing.
2 Metòd rechèch
2.1 pyès travay & machin
Alyaj: Inconel 718, 46 HRC, Ø 85 mm bar, 250 mm depase.
Tour: DMG CTX beta 800, 12 kW, 7 MPa atravè -awozaj zouti, 5 μm repetibilite pozisyon.
2.2 Koupe Zouti
| Paramèt | Karbid | Seramik |
|---|---|---|
| Mete | CNMG 120408-SF GC1115 | RNGN 120400 WH moustach-ranfòse Al₂O₃ |
| Kouch | TiAlN PVD | Okenn |
| Ang rato | -6 degre | -15 degre |
| Preparasyon Edge | 25 µm perfectionner | 10 µm chanfrein |
2.3 Pwosedi
De pase pou chak ba: ki graj a 1 mm stock, fini nan pwofondè final 0.2 mm.
Matrice faktori: vc 40, 60, 80, 100, 120 m/min × fn 0.05, 0.10, 0.15, 0.20 mm/r.
Kritè sispann: flan mete VB=0.3 mm oswa ka zo kase kwen.
Mezi: dinamomèt (Kistler 9129A) pou pouvwa, lazè profilomètr (Keyence LJ-V7080) pou Ra, X-difraksyon reyon pou kouch blan.
3 Rezilta ak analiz
3.1 Lavi zouti
Figi 1 montre lavi zouti kont vc. Karbid swiv yon pant Taylor klasik (n=0.24) k ap desann soti nan 24 min a 40 m/min rive 5 min nan 120 m/min. Seramik gaye ant 0.7-2.1 min pi wo a 80 m / min akòz krak tèmik.
3.2 Pousantaj retire materyèl (MRR)
Tablo 1 konpare MRR nan menm pwen zouti -fen lavi-.
| vc (m/min) | MRR carbure (cm³/min) | MRR seramik (cm³/min) | Rapò |
|---|---|---|---|
| 60 | 1.8 | 4.2 | 2.3 |
| 80 | 2.4 | 11.5 | 4.8 |
| 100 | 3.0 | 14.1 | 4.7 |
3.3 Sifas Entegrite
Ra (µm): carbure 0.42 ± 0.05; seramik 0.78 ± 0.12.
Blan-kouch pwofondè: <5 µm pou tou de; pa gen okenn ogmantasyon mezirab dite mikwo-.
Estrès rezidyèl: carbure kite 120 MPa konpresiv, seramik 180 MPa tansyon -toujou nan limit OEM.
3.4 Pouvwa trase
Carbide mwayèn 2.1 kW; seramik te monte nan 3.8 kW, nan rezèv spindle.
4 Diskisyon
4.1 Mete Mekanis yo
Karbid echwe pa mete flank ak mikro-chipping, ki konsistan avèk rapò Sandvik. Seramik sikonbe nan krak chòk tèmik pwopagasyon soti nan chanfrein la, akselere pa awozaj.
4.2 Kwaze Ekonomik-sou
Sèvi ak boutik-kourajman pri etaj (mete pri, chanje-avèk tan, to spindle), kraze-tè yo nan 110 m/min kote 3× MRR seramik depase pri 2× insert li ak pi gwo risk bouyon.
4.3 Limitasyon
Koupe kontinyèl sèlman; koupe koupe kraze seramik nan tès pilòt.
Presyon likid refwadisman > 8 MPa redwi lavi seramik pa 30%.
4.4 Takeaway pratik
Chwazi seramik lè (a) sifas Ra 0.8 µm akseptab, (b) file koton ka bay plis pase oswa egal a 100 m/min, (c) koupe yo kontinyèl. Baton nan carbure pou fini aérosol final oswa nenpòt travay plas/zepòl.
5 Konklizyon
Seramik foure twa pousantaj retire materyèl nan Inconel 718 pi wo a 80 m / min pandan y ap satisfè espesifikasyon blan -kouch, men sifas brutality ak risk ka zo kase favorize carbure pou Ra <0.5 µm oswa jeyometri koupe. Repwodui faktori a nan presyon likid refwadisman ou a pou konfime pwen kwazman an anvan re-site travay la.